FEP EW-1 / 2 / 3 / 4 (Standard Extrusion)
Perfluoroethylene-propylene resin (FEP)
- Optimal Melt Flow Index ：MFR: 0.8~2.0 g/10min
- Provides excellent wear resistance and material durability
- High-performance dielectric properties for demanding electrical applications
- Exceptional stability against heat and harsh chemical environments
Technical Specifications
Item | Unit | EW-1 | EW-2 | EW-3 | EW-4 | Test Method |
|---|---|---|---|---|---|---|
Appearance | / | Translucent Particle | Translucent Particle | Translucent Particle | Translucent Particle | / |
Melting Index (MFR) | g/10min | 2.1-4.0 | 4.1-8.0 | 8.1-12.0 | 12.1-20.0 | ASTM D2116 |
Tensile Strength | Mpa | ≥25.0 | ≥21 | ≥21 | ≥18.0 | ASTM D638 |
Elongation at Break | % | ≥300 | ≥300 | ≥300 | ≥280 | ASTM D638 |
Melting Point | ℃ | 265±10 | 265±10 | 265±10 | 260±10 | ASTM D3418 |
Relative Gravity | / | 2.12-2.17 | 2.12-2.17 | 2.12-2.17 | 2.12-2.17 | ASTM D792 |
Dielectric Constant（106Hz） | / | ≤2.15 | ≤2.15 | ≤2.15 | ≤2.15 | ASTM D150 |
Dissipation Factor（106Hz） | / | ≤7.0×10-4 | ≤7.0×10-4 | ≤7.0×10-4 | ≤7.0×10-4 | ASTM D150 |
Application
EW-1：Low melt extruding material, with good stress cracking resistance, mainly used for tubing, film, insulation and jacket of wire & cable.
EW-2：Low melt extruding material, with good stress cracking resistance mainly used for insulation and jacket of wire & cable, film and thin walled tube.
EW-3：Extruding material, with good stress cracking resistance, mainly used for insulation and jacket of wire & cable, tubing and film.
EW-4：Extruding material, mainly used for the insulation and jacket of wire & cable.
Packaging, Transportation and Storage
Package:
N.W.25kg/bag
1.It should be stored in a clean, dry, cool and light-shielded environment to prevent contamination by impurities.
2.Non-toxic, non-flammable, non-explosive and non-corrosive, it shall be transported as a non-dangerous good.